Functional Masterbatch for nylon 6 cable tie

MD-N06

MD-N06

Features

Production Introduction:

MD-N06 is specially designed for PA6 cable tie manufacturing, which delivers lower raw material cost, excellent flowability, faster cycle and easier mold release compared to un-modified Nylon 6 resin resulting in higher productivity and enhanced design freedom for injection molding customers. This resin also permits production of molded parts with good initial color plus color retention when using regrind.

Production Introduction:

MD-N06 is specially designed for PA6 cable tie manufacturing, which delivers lower raw material cost, excellent flowability, faster cycle and easier mold release compared to un-modified Nylon 6 resin resulting in higher productivity and enhanced design freedom for injection molding customers. This resin also permits production of molded parts with good initial color plus color retention when using regrind.

Specifications

Items

Test Method

Unit

Results （DAM）

Physical Properties

Specific gravity

ASTM D-792

 

~1.13

Mold shrinkage

ASTM D-955

%

1.0

Moisture uptake (24 hrs)

ASTM D-570

%

1.6

Mechanical Properties

Tensile modulus, 23℃

ASTM D-638

MPa (psi)

2600 (375,000)

Tensile strength @ yield, 23°C

ASTM D-638

MPa (psi)

75 (11,000)

Elongation @ break, 23°C

ASTM D-638

%

10

Flexural modulus, 23°C

ASTM D-790

MPa (psi)

2,600 (375,000)

Flexural strength, 23°C

ASTM D-790

MPa (psi)

100 (14,500)

Notched izod impact strength, 23°C

ASTM D-256

J/M

40 (0.75)

Thermal Properties

Melt point

ASTM D-3418

°C

220

Heat Deflection @ 264 psi (1.8 MPa)

ASTM D-648

°C

62

Heat Deflection @ 66 psi (0.45 MPa)

ASTM D-648

°C

175

Coef. Of Linear Thermal Expansion

ASTM E-831

μm/m °C

75

MD-N06 can be used for other thin-wall injection molding applications, including: Connectors, Plug housings, PCB spacers, Window components, and so on.

Below data are based on 10% MD-N06  blended with 90% Nylon 6.

Items

Test Method

Unit

Results （DAM）

Physical Properties

Specific gravity

ASTM D-792

 

~1.13

Mold shrinkage

ASTM D-955

%

1.0

Moisture uptake (24 hrs)

ASTM D-570

%

1.6

Mechanical Properties

Tensile modulus, 23℃

ASTM D-638

MPa (psi)

2600 (375,000)

Tensile strength @ yield, 23°C

ASTM D-638

MPa (psi)

75 (11,000)

Elongation @ break, 23°C

ASTM D-638

%

10

Flexural modulus, 23°C

ASTM D-790

MPa (psi)

2,600 (375,000)

Flexural strength, 23°C

ASTM D-790

MPa (psi)

100 (14,500)

Notched izod impact strength, 23°C

ASTM D-256

J/M

40 (0.75)

Thermal Properties

Melt point

ASTM D-3418

°C

220

Heat Deflection @ 264 psi (1.8 MPa)

ASTM D-648

°C

62

Heat Deflection @ 66 psi (0.45 MPa)

ASTM D-648

°C

175

Coef. Of Linear Thermal Expansion

ASTM E-831

μm/m °C

75

MD-N06 can be used for other thin-wall injection molding applications, including: Connectors, Plug housings, PCB spacers, Window components, and so on.

Below data are based on 10% MD-N06  blended with 90% Nylon 6.

Instructions

Typical Properties: (10% MB plus 90% PA6)

Values shown are based on limited testing. These provisional values are not intended for use in establishing maximum, minimum or ranges for specification purposes. Properties were measured at 23°C unless otherwise specified.

Typical Properties: (10% MB plus 90% PA6)

Values shown are based on limited testing. These provisional values are not intended for use in establishing maximum, minimum or ranges for specification purposes. Properties were measured at 23°C unless otherwise specified.