PA66 Impact Modifier

Test method

MD-S03

MD-S05

MD-AI0

MD-AH0

Density (g/cm3)

ISO1183

1.11

1.1

1.09

1.07

Filler content(%)

ISO1172

---

---

---

---

Mold shrinkage (%)

ISO294  Parallel

1.2

1.2

1.3

1.4

ISO294  Vertical

1.6

1.6

1.8

2

Tensile breaking strength (MPa)

ISO527  50mm/min

70

60

55

45

Elongation at break (%)

ISO527  50mm/min

20

30

40

60

Flexual strength (MPa)

ISO178        23℃ 10mm/min

80

70

60

50

Flexual modulus (MPa)

ISO178        23℃ 10mm/min

2500

2100

1900

1600

Notched Izod impact strength (JK/㎡）

ISO180  23℃

8

30

60

85

Izod impact strength

ISO179  23℃

NB

NB

NB

NB

Melting point (℃)

ISO11357-1

260

260

260

260

Distortion temperature (℃)

ISO75   0.45Mpa

180

170

170

130

ISO75   1.8Mpa

65

60

60

60

UL Flammability

UL-94

HB

HB

HB

HB

Glow-wire ignition temperature

IEC 60695-2-13

---

---

---

---

Surface resistivity (Ω)

IEC60093

1.00E+14

1.00E+14

1.00E+14

1.00E+14

Volume resistivity(Ω.cm)

IEC60093

1.00E+15

1.00E+15

1.00E+15

1.00E+15