PA66-M27

Color : nature

Shape: granulate

Processing method: Injection mold

Flame-retarded grade:

Color : nature

Shape: granulate

Processing method: Injection mold

Flame-retarded grade:

Features

PA66-M27 is specially designed for cable tie and delivers lower raw material cost, excellent flowability, faster cycle, low-temperature resistance and easier mold release for injection molding customers. This grade also permits production of molded parts with good initial color plus color retention when using regrind.

PA66-M27 is specially designed for cable tie and delivers lower raw material cost, excellent flowability, faster cycle, low-temperature resistance and easier mold release for injection molding customers. This grade also permits production of molded parts with good initial color plus color retention when using regrind.

Specifications
Physical property Testing Date Unit
relative density ISO1183 1. 13 g/cm3
shrinkage rate flow 2.0mm 23C ISO 294 1.7 %
shrinkage rate vertical 2.0mm 23C ISO 294 1.8 %
water absorption 23C 24hr ISO 62 1.2 %
water absorption 23C 50RH ISO 62 2.4 %
Mechanical features Testing Dry/Wet Unit
Flexural strength 23C ISO 178 100 MPa
Flexural modulus 23C ISO 178 2700 MPa
Charpy Notched Impact Strength -30C ISO 179 4.4 kj/m3
Charpy Notched Impact Strength 23C ISO 179 NB kj/m3
drying temperature   90 C
drying time   6- 10 hr
First stage temperature   260-280 C
Second stage temperature   270-285 C
Third stage temperature   280-290 C
nozzle temperature   280-300 C
melting temperature   285-300 C
mold temperature   65-95 C
maximum recovery rate   50 %
Physical property Testing Date Unit
relative density ISO1183 1. 13 g/cm3
shrinkage rate flow 2.0mm 23C ISO 294 1.7 %
shrinkage rate vertical 2.0mm 23C ISO 294 1.8 %
water absorption 23C 24hr ISO 62 1.2 %
water absorption 23C 50RH ISO 62 2.4 %
Mechanical features Testing Dry/Wet Unit
Flexural strength 23C ISO 178 100 MPa
Flexural modulus 23C ISO 178 2700 MPa
Charpy Notched Impact Strength -30C ISO 179 4.4 kj/m3
Charpy Notched Impact Strength 23C ISO 179 NB kj/m3
drying temperature   90 C
drying time   6- 10 hr
First stage temperature   260-280 C
Second stage temperature   270-285 C
Third stage temperature   280-290 C
nozzle temperature   280-300 C
melting temperature   285-300 C
mold temperature   65-95 C
maximum recovery rate   50 %
Instructions

Packing and storage: 25kgs ,composite paper-plastic bag.
Protect from rain, moisture,and sun.
Store in a dry and cool enviroment as general chemicals.

Packing and storage: 25kgs ,composite paper-plastic bag.
Protect from rain, moisture,and sun.
Store in a dry and cool enviroment as general chemicals.